SCOPE OF USE
Inside or outside coatings on:
• Drinking water reservoirs.
• Water tanks.
• Swimming pools.
• Saunas and jacuzzis.
• Tunnels.
Waterproofing of terraces, balconies and wet areas. Waterproofing of sludge basins in sewage. Waterproofing of below-grade structures like basements,
retaining walls, foundations, etc…
PROPERTIES
• Approved for contact with potable water
• Resists high hydrostatic positive and negative pressures
• Long working life
• Excellent crack accommodation before and after immersion
• Excellent adhesion to sound, prepared substrates: does not require bonding agents and can be applied on wet surfaces
• Permeable to water vapor, allows the substrate to breathe.
• Resistant to abrasion
• Withstands occasional foot traffic
• Reduces carbonation and electrochemical corrosion
• Environmentally friendly: Non-toxic and chloride-free
WEBERDRY 110FX
Brand:
Description
weberdry 110 FX is a two component polymer modified cementitious coating:
• Powder made of cements, fillers and admixtures.
• Liquid based on resins and additives.
It is available in Grey and White
weberdry 110 FX cures to form an elastomeric, waterproof, flexible and resistant membrane, suitable for use in potable water tanks, reservoirs, canals and tunnels. The material which can be applied on cement based substrate like concrete, cement plaster, masonry and cementboards (with primer) substrates has been designed to accommodate good crack bridging qualities even after long term water immersion. weberdry 110 FX must be used on damp cement based substrates. The adhesion and sealing qualities of weberdry 110 FX are outstanding. Therefore, it can be used for positive or negative hydrostatic pressures. The material prevents reinforcements from corrosion.
| Size/Dimensions | powder (A) 15 kg + 9.8 kg liquid (B)= 24.8 kg |
|---|---|
| color | grey, White |
| Powder appearance | White or grey |
| Mixed Density at 24°C | 1600 ± 100 kg/m³ |
| Minimum Application temp | + 5 °C |
| Tensile Strength | > 1.60 N/mm2 (with mesh) (ASTM D 412) |
| Pull off Strength | 1 ± 0.2 MPa @ 28 days on concrete substrate |
| Elongation at break | above 200 % (without mesh) |
| Crack bridging Ability 3 mm | No sign of cracking, splitting, pinholes were observed (with out mesh) |
| VOC | Low emitting material |